White Fused Aluminum Oxide (WFA) is produced from the melting of high purity calcined alumina in electric arc furnaces. It is characterized by its high hardness, friable, high purity, chemical stability, high melting point and large crystal size.
White cast aluminum oxide is used in many applications, including grinding and cutting wheels, refractory materials and ceramic forms, coated abrasives, investment cast coatings, laminates, coatings, blasting, polishing and lapping abrasives, etc. Please see below for product information related to your request.
1. Bonded abrasive tools.
2. Coated abrasive tools.
3. Refractory and Ceramic.
4. White aluminum oxide obtained from the fusion of calcined alumina in electric arc furnaces. It is recommended for refractory applications where purity, chemical stability, or high refractoriness are a matter to consider.
5. Polishing glass and the electronics industry.
6. Special micro power for precision foundation.
232/5000
Bonded abrasives
Typical chemical analysis by weight% (F24):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
Na 2
Typical value
99.52
0.08
0.04
0.33
Typical chemical analysis in% by weight (JIS1200):
Index
Al2O3
SiO2
Fe2O3
Na2O
Typical value
99.34
0.12
0.09
0.45
Available grains: F4 a F220, F230 a F1200, JIS240 a JIS8000.
In accordance with current GB / FEPA / JIS sieve standards.
Coated abrasives
Typical chemical analysis by weight% (P80):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
Na2O
Typical value
99.52
0.08
0.06
0.33
Available grains: P12 a P220,P240 a P2500.
In accordance with current GB / FEPA / JIS sieve standards.
Sandblasting
Typical chemical analysis by weight% (F24):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
Na2O
Typical value
99.39
0.08
0.08
0.31
Available grains: F4 a F220, F230 a F1200, JIS240 a JIS8000.
In accordance with current GB / FEPA / JIS sieve standards.
Refractories
Typical chemical analysis by weight% (1-3 mm):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
Na2O
Typical value
99.29
0.045
0.05
0.29
Available grains: 0-1mm,1-3mm,3-5mm,5-8mm,200mesh,325mesh.
Other sizes are also available on request.