Brown molten aluminum oxide is produced by melting high-quality bauxite in an electric arc furnace at high temperatures. It is of compressive strength, high toughness, good self-sharpening, lower coefficient of expansion, no rusty stain, good hydrophilicity, high cleaning, heat resistance and chemical stability, etc.
Suitable for many different applications such as: grinding wheels, sandpaper, blasting media, metal preparation, polishing, polishing and grinding. Due to its thermal properties, it can also be used for refractory applications.
Bonded abrasives
Typical chemical analysis by weight % (F24):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
TiO 2
BFA-Resin
95.50
1.05
0.12
2.43
BFA-Vitrified
95.45
0.88
0.17
2.59
Available grains: F12 a F220, F230 a F1500, #240 a #3000
Coated abrasives
Typical chemical analysis by weight% (P40):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
TiO 2
Typical value
95.71
0.81
0.10
2.38
Available grains: P12 a P220, P240 a P1500.
In accordance with current GB / FEPA / JIS sieve standards.
Sandblasting
Typical chemical analysis by weight% (F24):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
TiO 2
BFA
95.50
1.05
0.14
2.43
Available grains: F12 a F220, F240 a F1500.
In accordance with current GB / FEPA / JIS sieve standards.
Refractories
Typical chemical analysis by weight% (1-3 mm):
Index
Al 2 O 3
SiO 2
Fe 2 O 3
TiO 2
BFA
95.50
0.85
0.14
2.2
Available grains: 0-1 mm, 1-3 mm, 3-5 mm, 5-8 mm, 0-3 mm, 0-5 mm, 0-10 mm, 0-25 mm, 180 malla, 200 malla.
Other sizes are also available on request.